Schenectady after breaking in two.
Schenectady after breaking in two.
Schenectady after breaking in two.
History
United States
NameSchenectady
OwnerWar Shipping Administration
Ordered24 March 1942
BuilderKaiser Shipyards
Cost$2,700,000
Yard number1
Laid down1 July 1942
Launched24 October 1942
Sponsored byMrs Alex B. McEachern
Completed31 December 1942
FateScrapped in 1962
General characteristics
Class and typeT2 tanker
TypeT2-SE-A1
Tonnage10,448 GRT / 16,613 DWT
Length523 ft (159 m)
Beam68 ft (21 m)
Installed power6,000 hp (4,500 kW)
Speed15 knots (28 km/h)
Range12,600 nautical miles (14,500 mi; 23,300 km)

The SS Schenectady was a T2-SE-A1 tanker built during World War II for the United States Maritime Commission.

She was the first tanker constructed by the Kaiser Shipbuilding Company shipyard at the Swan Island Shipyard in Portland, Oregon.[1] The keel of the Schenectady was laid on 1 July 1942, the completed hull launched on 24 October, and she was declared completed on 31 December, six months after construction began and two and a half months ahead of schedule.[2]

Hull fracture

On 16 January 1943, she was moored at the fitting dock at Swan Island, in calm weather, shortly after returning from her sea trials. Without warning, and with a noise audible for at least a mile, the hull cracked almost in half, just aft of the superstructure. The cracks reached down the port and starboard sides almost to the keel, which itself fractured, jackknifing upward out of the water as the bow and stern sagged to the bottom of the river. Only the bottom plates of the ship held. This was not the first of the war-built merchant fleet to fracture in this way there had been ten other major incidents, and several more would follow but it was perhaps the most prominent; it occurred in full view of the city of Portland, and was widely reported in the newspapers even under wartime conditions.[3]

The cause of the fracture was not fully understood at the time; the official Coast Guard report gave the cause of failure as faulty welding, while the Board of Investigation considered factors as diverse as "locked-in" stresses, sharp changes in climate, or systemic design flaws. Defective welding became the most common explanation for these incidents, especially when later investigations uncovered faulty working practices at some yards, but even then it could only be clearly identified as the case in under half of all major fracture cases. Later research indicated that the failure method was probably a brittle fracture, caused by low-grade steel. This would become highly brittle in cold weather, exacerbating any existing faults and becoming much more liable to fracture.[3][4]

Later service

She was repaired and successfully entered service in April 1943.[1]

Details of her exact service are unclear, but it is known that she sailed from California on June 10, 1944, possibly for service as a fleet oiler. During the next year, she sailed to Australia, the Persian Gulf, New Zealand, the Marshall Islands, then Curaçao, back through the Panama Canal to the Marshall Islands, the Caroline Islands, the Admiralty Islands and finally Ulithi, before returning home to San Pedro, arriving on May 20, 1945. She participated in battle engagements in the Marshall Islands and at Ulithi.[5]

Following the war, she was transferred to the National Defense Reserve Fleet in July 1946.[6] In 1948, she was sold to the Diodato Tripcovich Shipping Corporation in Trieste, and renamed as Diodato Tripcovich. She was finally scrapped in Genoa in 1962.[7]

References

  1. 1 2 Fingering The S. S. Schenectady Archived 2012-02-17 at the Wayback Machine, Portland Communique. May 20, 2005.
  2. Database entry at us-maritime-commission.de
  3. 1 2 Thompson, Peter (2001). "How Much Did the Liberty Shipbuilders Learn? New Evidence for an Old Case Study". The Journal of Political Economy. The University of Chicago Press. 109 (1): 103–137. CiteSeerX 10.1.1.197.1438. doi:10.1086/318605. JSTOR 3078527.
  4. Murray, Charles (March 5, 2015). "Engineering Disasters: SS Schenectady, a Lesson in Brittle Fracture". Design News. Informa Markets. Retrieved 18 November 2022.
  5. Notes made in the statement of fact in the case of Carmichael v. Delaney, United States Court of Appeals, Ninth Circuit, 18 October 1948. Quoted on p.271 of International Law Reports, by H. Lauterpacht & Christopher J. Greenwood. Cambridge University Press, 1951. Online edition
  6. Database entry Archived 2011-07-21 at the Wayback Machine at PMARS.
  7. Database entry at Auke Visser's Famous T-Tankers Pages


This article is issued from Wikipedia. The text is licensed under Creative Commons - Attribution - Sharealike. Additional terms may apply for the media files.